Density Optimization of Lithium Lanthanum Titanate Ceramics for Lightweight Lithium-Air Batteries

Report No. ARL-TR-7145
Authors: Claire Weiss Brennan; Victoria Blair; Joseph Marsico
Date/Pages: November 2014; 22 pages
Abstract: The US Army has an urgent need for robust, high-energy-density, lightweight energy storage devices, and the lithium (Li)-air battery is one promising solution due to its high-energy density and lower weight compared with Li-ion batteries. The ceramic electrolytic membrane is currently the bottleneck for successful implementation of Li-air batteries. The density of the electrolytic membrane material, Li0.35La0.57TiO3 (LLTO), must be optimized for LLTO to attain its maximum ionic conductivity because previous work done by the US Army Research Laboratory has demonstrated a relationship between density and conductivity in LLTO. The sintering behavior of LLTO requires comprehensive study to synthesize dense ceramics with high ionic conductivity. Therefore, the sintering temperature was varied from 1,100 °C to 1,350 °C, and the density of LLTO pellets was measured using 3 different techniquesX-ray diffraction, optical microscopy, and scanning electron microscopy, which were also used to determine the phases, crystal structure, crystallite size, and microstructure of the sintered LLTO pellets. It was found that sintering at 1,200 °C produced tetragonal LLTO ceramics with the highest densitymore than 95% of the theoretical density. Lower sintering temperatures yielded LLTO samples with lower densities and smaller crystallite sizes. Sintering at 1,300 °C produced concave pellets with slight preferred crystallographic orientation.
Distribution: Approved for public release
  Download Report ( 0.949 MBytes )
If you are visually impaired or need a physical copy of this report, please visit and contact DTIC.
 

Last Update / Reviewed: November 1, 2014