The Sintering and Densification Behavior of an Iron Nanopowder Characterized by Comparative Methods

Report No. ARL-TR-2909
Authors: Laszlo J. Kecskes, Robert H. Woodman, Samuel F. Trevino, Bradley R. Klotz, and S. Gary Hirsch
Date/Pages: February 2003; 40 pages
Abstract: Fe nanopowder, derived from microwave plasma synthesis (Materials Modifications Inc., Fairfax, VA), was obtained and characterized for particle size and size distribution. The methods used included static light scattering (SLS) and dynamic light scattering (DLS), surface area and size by Brunauer, Emmett, and Teller (BET) analysis, small angle neutron scattering (SANS), neutron diffraction (ND), x-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM). Based on these methods, it was concluded that the Fe powder was composed of nanosized particles, but in micrometer-sized aggregates. DLS indicated a mean agglomerate size with a single mode distribution of 70 ? 6 nm. In contrast, SLS revealed a wide bimodal distribution ranging from 0.5 to 20 ?m. The mean particle sizes that resulted from BET and XRD analyses were 60 and 20 nm, respectively. SANS, in combination with ND, determined that the powder had a bimodal distribution of mean size 24 and 64 nm. TEM and FESEM confirmed that the powder is composed of 50- to 80-nm particles that is found in large, dendritic particle agglomerates which are on the order of micrometers. Subsequent to characterization, the sinterability and densification behavior of the Fe nanopowder was examined by further experimentation wherein powder compacts were pressureless sintered under hydrogen. Results showed that without pressure, the powder could not be sintered to full density, however, the densification of the Fe powder strongly depended on the temperature. There was little or no coarsening below 500 ?C. In contrast, significant grain growth was observed in the samples above that temperature. In further experiments, using a plasma pressure compaction (P2C) apparatus, the powder was consolidated to final densities near 80% of the theoretical full density. The observed limitations in the densification and associated porous microstructures of the pressureless-sintered and P2C-densified compacts were rationalized in terms of the
Distribution: Approved for public release
  Download Report ( 2.576 MBytes )
If you are visually impaired or need a physical copy of this report, please visit and contact DTIC.

Last Update / Reviewed: February 1, 2003